LF3铝合金腐蚀过程声发射特性研究
建立了用声发射监测金属腐蚀过程的方法，结合LF3铝合金在不同浓度硝酸溶液中的腐蚀过程声发射实验数据，对声发射信号特征参数进行了统计分析和相关分析，得出了LF3铝合金腐蚀过程声发射信号特征参数随腐蚀介质浓度变化的统计规律。
Study on Acoustic Emission Characteristic of LF3 Aluminium Alloy Corrosion Process
Yang Nengjun，Wang Hangong，Gao Chengqiang, Liu Xiaofang
(Section 501, Second Artillery Engineering College, Xi’an, 710025)
Abstract：A new method for corrosion inspection with acoustic emission technology is set up. Based on the acoustic emission experimental data of LF3 alloy with different concentrations of nitric acid, statistic analysis and correlation analysis are processed with the characteristic parameters of acoustic emission signal, and the statistical law between characteristic parameters of acoustic emission signal in LF3 corrosion process and density of corrosive is drawn out.
Keywords：LF3 alloy，Corrosion，Acoustic emission，Characteristic parameter
[1]。
2Al3），另外还存在MnAl6、Mg2Si相。LF3合金的耐蚀性与β相的析出和分布有关。此外，LF3合金的杂质中，铁与铝几乎不生成固溶体而是形成金属间化合物FeAl3，Cu进入铝中形成固溶体，这两者均会降低LF3的耐腐蚀性。
表1 LF3化学成分（％）
主要化学成分 | 杂质（不大于） | |||||
Mg | Mn | Si | Al | Fe | Cu | 其他杂质 |
3.48 | 0.48 | 0.57 | 余量 | 0.5 | 0.05 | 0.1 |
2 腐蚀声发射信号特征参数的分布分析
为比较不同特征参数之间的差异程度，对不同硝酸浓度水平下获得腐蚀声发射信号的特征参数进行相关分析，结果见表2。其中，参数A、R、D、CNTS、E分别为声发射信号的幅度、上升时间、持续时间、振铃计数和能量。由表2可见，对所有浓度水平，持续时间、振铃计数、能量这三个参数的相关性均较强，幅度和振铃计数也有一定的相关。对10.0%、19.8%这两个浓度，幅度和振铃计数、幅度和能量、持续时间和能量、振铃计数和能量分别强相关；对5.0%的浓度，持续时间和能量、振铃计数和能量分别强相关；对0.1%—3.0%的浓度，持续时间、振铃计数、能量三个参数表现为相关，其他的特征参数没有表现明显